Development of a Chitosan/Nickel Phthalocyanine Composite Based Conductometric Micro-sensor for Methanol Detection

Thin-film composite of chitosan/nickel phthalocyanine (NiPc) was electrochemically deposited on the fingers of interdigitated gold electrodes, applying chronoamperometric polymerization technique. The presence of crystallized NiPc in the chitosan was confirmed by EDX and FTIR analysis. Acetone, ethanol, and methanol gas-sensing properties of the films prepared at optimum conditions were studied at atmospheric temperature, through differential measurements at an optimized frequency of 10 kHz, using a lock-in amplifier. The conductometric sensor presents the highest sensitivity of 60.2 μS.cm⁻¹(v/v) for methanol and 700 ppm as the limit of detection. For validation, the methanol content of a commercial rubbing alcohol was determined.     

气相输运沉积制备c轴择优取向的碘化铋薄膜

铋基卤化物材料因其无毒和优良的光电性能而显示出巨大的应用潜力。BiI₃作为一种层状重金属半导体,已被用于X射线检测、γ射线检测和压力传感器等领域,最近其作为一种薄膜太阳能电池吸收材料备受关注。本文采用简单的气相输运沉积(VTD)法,以BiI₃晶体粉末作为蒸发源,在玻璃基底上得到高质量c轴择优取向的BiI₃薄膜。并通过研究蒸发源温度和沉积距离对薄膜物相和形貌的影响,分析了BiI₃薄膜择优生长的机理。结果表明VTD法制备的BiI₃薄膜属于三斜晶系,其光学带隙为~1.8 eV。沉积温度对薄膜的择优取向有较大影响,在沉积温度低于270 ℃时,沉积的薄膜具有沿c轴择优取向生长的特点,超过此温度,c轴择优取向生长消失。在衬底温度为250 ℃、沉积距离为15 cm时制备的薄膜结晶性能最好,晶体形貌为片状八面体。     

雾化辅助化学气相沉积法氧化镓薄膜生长研究

采用自主设计搭建的雾化辅助化学气相沉积系统设备,开展了Ga₂O₃薄膜制备及其特性研究工作。通过X射线衍射研究了沉积温度、系统沉积压差对Ga₂O₃薄膜结晶质量的影响。结果表明,Ga₂O₃在425~650 ℃温度区间存在物相转换关系。随着沉积温度从425 ℃升高至650 ℃,薄膜结晶分别由非晶态、纯α-Ga₂O₃结晶状态向α-Ga₂O₃、β-Ga₂O₃两相混合结晶状态改变。通过原子力显微镜表征探究了生长温度对Ga₂O₃薄膜表面形貌的影响,从475 ℃升高至650 ℃时,薄膜表面粗糙度由26.8 nm下降至24.8 nm。同时,高分辨X射线衍射仪测试表明475 ℃、5 Pa压差条件下的α-Ga₂O₃薄膜样品半峰全宽仅为190.8″,为高度结晶态的单晶α-Ga₂O₃薄膜材料。     

光纤基底TiNi形状记忆合金薄膜制备工艺

将TiNi基记忆合金薄膜与光纤相结合可制成智能化、集成化且成本经济的微机电系统和微传感器件.本文采用磁控溅射法在二氧化硅光纤基底上制备TiNi记忆合金薄膜,系统讨论了溅射工艺参数以及后续退火处理对薄膜质量的影响.采用自研制光纤镀膜掩膜装置在直径为125μm的光纤圆周表面上形成均匀薄膜.实验表明:在靶基距、背底真空度、Ar气流量和溅射时间一定的条件下,溅射功率存在最佳值;溅射压强较大时,薄膜沉积速率较低,但薄膜表面粗糙度较小.进行退火处理后,薄膜形成较良好的晶体结构,Ti_49.09Ni_50.91薄膜中马氏体B19′相和奥氏体B2相共存,但以B19′为主.根据本文研究结果,在玻璃光纤基底上制备高质量的TiNi基记忆合金薄膜是可实现的,本工作为下一步研制微机电系统和微型传感器做了基础准备.     

基于抛光基材的热蒸镀铜箔生长高平整单层石墨烯薄膜

在石墨烯的化学气相沉积工艺中,铜箔是决定石墨烯薄膜质量的重要因素。传统铜箔由于制备工艺的限制,存在大量的缺陷,导致石墨烯薄膜的成核密度较高。本工作选用抛光铝板、抛光不锈钢板、微晶玻璃和SiO₂/Si作为基材,用热蒸镀法制备了不同粗糙度的铜箔,并详细讨论了以该系列铜箔生长高平整度石墨烯薄膜的条件及铜箔对石墨烯薄膜品质的影响。实验结果表明,铜箔以(111)取向为主,与基材分离后,表面具有纳米级平整度。在生长石墨烯后,从SiO₂/Si剥离的铜箔成核密度是4种基材中最小的。同时,从SiO₂/Si剥离的铜箔晶体结构变化最不明显,具有良好的结晶性,表面几乎不存在铜晶界缺陷。当压强为3 000 Pa,氢气和甲烷流速分别为300 mL/min和0.5 mL/min时,可以获得约1 mm横向尺寸的石墨烯单晶晶畴。     

硫化镉反蛋白石光子晶体制备及光解水制氢

对硫化镉反蛋白石结构光子晶体薄膜进行了可控合成,用巯基乙酸修饰的纳米晶和P(St-MMA-SPMAP)高分子小球共组装,成功地构筑了反蛋白石结构并用于可见光光解水产氢。结果表明,在可见光(λ≥420 nm)照射下,Cd S-310反蛋白石结构薄膜的光解水产氢性能比硫化镉纳米颗粒提高了一倍。这主要是因为等级孔结构反蛋白石光子晶体特性对催化剂的光催化性能的提升:首先,反蛋白石的周期性结构增加了光子在材料中的传播,提高了催化剂对太阳光的利用率;同时,大孔孔壁是由纳米颗粒堆积而成的,在反应中提供了更多的反应活性位点;此外,孔结构有利于物质的传输和分子的吸附。     

Highly Sensitive AdSV Method for Fe(III) Determination in Presence of Solochrome Violet RS on Renewable Amalgam Film Electrode

The new DP AdSV method for high sensitive Fe(III) determination in the presence of Solochrome Violet RS was developed. The use of an innovative renewable amalgam film electrode Hg(Ag)FE allowed to obtain high sensitivity and significantly minimize the mercury consumption. The best results were obtained for surface area of Hg(Ag)FE equal to 11.8 mm². Instrumental parameters were optimized. The optimal results were obtained using differential pulse technique for the following values: sampling and waiting time ts=tw=10 ms, step potential Es=5 mV, pulse amplitude ΔE=50 mV. Measurements were conducted in 0.05 M acetate buffer (pH 5.6), the concentration of SVRS was equal to 5 μM. Deposition step was carried out at the potential ?400 mV for 20 s. Calculated detection limit for 40 s preconcentration time was equal to 1.4 nM (78 ng L^?1). The influence of the common in environment, organic and inorganic interferences was studied. The developed method for Fe(III) determination was successfully applied and validated by investigation of certified reference material SPS‐SW2 Batch 118 and recovery of Fe(III) from various spiked samples as snow, tap water and bottom sediments. The repeatability (for 50 nM of Fe(III)) of the developed method expressed as CV was equal 3.1 % (n=5).     

Improving the gas barrier,mechanical and thermal properties of poly(vinyl alcohol) with molybdenum disulfide nanosheets

New multifunctional materials with both high structural and gas barrier performances are important for a range of applications. Herein we present a one‐step mechanochemical process to prepare molybdenum disulfide (MoS₂) nanosheets with hydroxy functional groups that can simultaneously improve mechanical strength, thermal conductivity, and gas permittivity of a polymer composite. By homogeneously incorporating these functionalized MoS₂ nanosheets at low loading of less than 1 vol %, a poly(vinyl alcohol) (PVA) polymer exhibits elongation at break of 154%, toughness of 82 MJ/m³, and in‐plane thermal conductivity of 2.31 W/m K. Furthermore, this composite exhibits significant gas barrier performance, reducing the permeability of helium by 95%. Under fire condition, the MoS₂ nanosheets form thermally stable char, thus enhancing the material's resistance to fire. Hydrogen bonding has been identified as the main interaction mechanism between the nanofillers and the polymer matrix. The present results suggest that the PVA composite reinforced with 2D layered nanomaterial offers great potentials in packaging and fire retardant applications. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2019 , 57, 406–414     

掺锗提高VO2薄膜的相变温度机理研究

二氧化钒(VO₂)作为一种长久以来备受关注的新型可逆相变材料,发展潜力巨大,其相变温度(T_MIT)的调控一直是研究热点。本文主要利用锗离子作为掺杂离子探索其对VO₂薄膜T_MIT的影响,并尝试解释其内部作用机理。在约1 cm²大小抛光的氧化铝薄片上沉积了一系列含不同比例锗离子VO₂薄膜。研究发现锗离子作为掺杂离子确实有利于T_MIT的提高(本课题T_MIT最大可达84.7 ℃)。T_MIT提高的主要原因是锗离子的引入能够强化单斜态V-V二聚体的稳定性,进而增强单斜态的稳定性,使得低温单斜态向四方金红石态转变更加困难。     

Densitometry and indirect normal‐phase HPTLC–ESI–MS for separation and quantitation of drugs and their glucuronide metabolites from plasma

The present work describes novel methods using densitometry and indirect or off‐line high performance thin‐layer chromatography–mass spectrometry (HPTLC–MS) for the simultaneous detection and quantification of asenapine, propranolol and telmisartan and their phase II glucuronide metabolites. After chromatographic separation of the drugs and their metabolites the analytes were scraped, extracted in methanol and concentrated prior to mass spectrometric analysis. Different combinations of toluene and methanol–ethanol–n‐butanol–iso‐propanol were tested for analyte separation and the best results were obtained using toluene–methanol–ammonia (6.9:3.0:0.1, v/v/v) as the elution solvent. All of the drug–metabolite pairs were separated with a homologous retardation factor difference of ≥22. The conventional densitometric approach was also studied and the method performances were compared. Both of the approaches were validated following the International Conference on Harmonization guidelines, and applied to spiked human plasma samples. The major advantage of the TLC–MS approach is that it can provide much lower limits of detection (1.98–5.83 pg/band) and limit of quantitation (5.97–17.63 pg/band) with good precision (?3.0% coefficient of variation) compared with TLC–densitometry. The proposed indirect HPTLC–MS method is simple yet effective and has tremendous potential in the separation and quantitation of drugs and their metabolites from biological samples, especially for clinical studies.